DNV offers a scope of answers for fluids including juices, soda pops, soups (both frosty and hot fill).

The bundling of fluids, including juices, soda pops and soups, are experiencing enormous transformations.Modern bundling, for example, stand-up pockets or Doy-packs are the most looked for after in this fragment. Zero dampness entrance and snugness of pressing are critical to our customers. Besides, as espresso and flavors in which smells assume a vital part require bundling to ensure against entrance of outside scents. Connected bundling sorts are as per the following:

  • » Stand-up pouches or Doy-pack;
  • » Coffee vacuum packaging;
  • » Flow-pack (VFFS)
  • » Doy packs

Technology: PET/Foil/PE, BOPP/PE/PET/PE , Paper/BOPP , PE, PET/BOPP, Paper/PE/Foil/PE, BOPP/BOPP, BOPP/PE, BOPP/ET.

MATERIALS & STRUCTURES

BOPP/ET

  • 1. Varnish finish. Thickness:: 1 µm
  • 2. Ink. Thickness: 1 µm
  • 3. Transparent/MET/pearl BOPP film. Thickness:: 35-38 µm

Bottle labels

  • Outstanding whiteness and opacity, wearing quality
  • High wet fastness of film and ink layer
  • Maximum output on the machinery

BOPP/BOPP

  • 1. Varnish finish. Thickness: 1 µm
  • 2. Ink. Thickness: 1 µm
  • 3. White/transparent/MET/MAT BOPP film. Thickness: 15-30 µm
  • 4. Ink. Thickness: 1 µm
  • 5. Adhesive. Thickness: 2-4 µm
  • 6. Ink. Thickness: 1 µm
  • 7. Transparent/MET BOPP film. Thickness: 15-35 µm

Tea.

  • Superior barrier performance
  • Allows for interlayer printing, helping ink layers stay intact throughout processing
  • Outstanding packaging strength and highly puncture resistant
  • Highly water vapour resistant
  • Matte finish available
  • Higher output along with more flexible weight (based on expanded structure)
  • High barrier performance against gases
  • Low moisture permeability
  • Protection from direct sunlight
  • High protection from aromas and odours
  • Allows for inert gases within the package itself

BOPP/PE

  • 1. Transparent BOPP film. Thickness: 20 µm
  • 2. Ink. Thickness: 1 µm
  • 3. Ink. Thickness: 1 µm
  • 4. White/transparent/MET/MAT BOPP film. Thickness: 15-30 µm

Coffee, cacao and dry crystals.

  • High barrier performance
  • Attractive shelf appearance (gloss, etc.)
  • High-strength
  • Interlayers do not lose integrity when exposed to friction or low temperatures
  • Excellent machinability and stable slip coefficient for filling equipment
  • High weld strength at low temperatures and during pouch-formation (hot tack)
  • Puncture resistant

BOPP/PE/PET/PE

  • 1. Transparent BOPP film. Thickness: 20 µm
  • 2. Ink. Thickness: 1 µm
  • 3. Adhesive (PE melted on extrusion laminator). Thickness: 2-4 µm
  • 4. Transparent PET Polyethylene Terephtalate film. Thickness: 12 µm
  • 5. Transparent PE film. Thickness: 10-50 µm

Tea.

  • Superior barrier performance
  • Packs very tightly
  • Cost-effective
  • Very good machinability on filling equipment

PET/Foil/PE

  • 1. Transparent PET Polyethylene Terephtalate film. Thickness: 12 µm
  • 2. Ink. Thickness: 1 µm
  • 3. Adhesive. Thickness: 2-4 µm
  • 4. MET Foil. Thickness: 7 µm
  • 5. Adhesive. Thickness: 2-4 µm
  • 6. White PE film. Thickness: 60-130 µm

Coffee, cacao and dry crystals.

  • Packaging withstands exposure to abrasive chemicals
  • Aroma resistant
  • Very hygienic
  • High-strength, tight welds
  • Tear resistant
  • Rigid, with puncture resistance
  • Stable packaging shape

Paper/BOPP

  • 1. Varnish finish. Thickness: 1 µm
  • 2. Ink. Thickness: 1 µm
  • 3. White paper. Thickness: 40 µm
  • 4. Adhesive. Thickness: 2-4 µm
  • 5. MET/AlOx. Thickness: 0,05 µm
  • 6. MET BOPP film. Thickness: 20 µm

Tea.

  • Superior barrier performance
  • Packs very tightly
  • Cost-effective
  • Very good machinability on filling equipment

Paper/PE/Foil/PE

  • 1. Varnish finish. Thickness: 1 µm
  • 2. Ink. Thickness: 1 µm
  • 3. White paper. Thickness: 40-50 µm
  • 4. Adhesive (PE melted on extrusion laminator). Thickness: 2-4 µmm
  • 5. MET/AlOx. Thickness: 0,05 µm
  • 6. MET foil. Thickness: 7 µm

Coffee, cacao, dry crystals.

  • High-strength
  • Strong, tight weld
  • Very high elasticity
  • Cost-effective
  • Excellent machinability and stable slip coefficient for filling equipment

PE

  • 1. Transparent PE. Thickness: 60-70 µm

Shrink case packing.

  • Superior barrier performance
  • Packs very tightly
  • Cost-effective
  • Very good machinability on filling equipment

PET/BOPP

  • 1.Transparent PET Polyethylene Terephtalate. Thickness: 12 µm
  • 2.Ink. Thickness: 1 µm
  • 3.Adhesive. Thickness: 2-4 µm
  • 4.Transparent/MET BOPP films. Thickness: 15-40 µm

Tea.

  • High barrier properties
  • Excellent strength characteristics
  • High- strength packaging with high puncture resistance
  • Cost-effective
  • Eye-catching finish